Product Details:
Minimum Order Quantity | 100 Kg |
Thickness | As per requirement (0.5 mm to 100 mm) |
Material | RESIN |
Color | AS PER REQUIREMENT |
Shape | Other |
Surface Treatment | As per requirement |
Density | Medium |
Size | As per requirement |
Warranty | NOT APPLICABLE |
Brand | SADHANA |
Product Type | FRP |
Resin Type | Epoxy Resin |
Temperature Limit | 100 DEGREE CELCIOUS |
Is It Transparent | Non Transparent |
We are sadhana fibre glass industries, manufacture of Epoxy Sheet as per per IS : 10192 : 1982 Epoxy Glass Cloth Laminated Sheet is made of alkali-free E-glass cloth impregnated with epoxy resins by processing under heat and pressure. This product having high mechanical and dielectric properties,fine heat and humidity resistance, can be used in electrical machine and devices as insulating construction parts in moist circumstances and in transformer oil. .
Applications:With high mechanical strength, Insulation, heat resistance, electrical properties and good moisture resistance properties. Widely range of applications, for example: Suitable for using as insulating structural parts in electric equipment, such as electric generators, motors, switch board, pcb, etc
- Sheets Thickness : 0.3-100mm;
- Width : 1220mm & 1530mm
- Length: 13foot
- Technical Specification : as per IS 10912 : 1982
Specific gravity 1.7, Water Absortion for 1.5mm thickness sheet is 0.40%. for 3 - 5mm thickness sheet is 0.30%,for 5 - 10mm thickness sheet it is 0.20%.Tensile Strength, N/mm2 200. Cross Braking Strength, N/mm2 300. Compressive Strength, N/mm2 350. Electric Strength - KV/mm 10 (FLATWISE upto 5mm thickness). Thermal: 150 degree to 200 degree C
Flammability :- Average time of burning (ATB)Sec.
- Average Extent of burning(AEB) min. NIL 10 9. Martens heat Distortion Temperature, 90 ºC 170
Availability :-- Epoxy: 0.3 to 100mm size thickness / width 1000 /1530 mm.
We can supply Epoxy sheeet as per our customer requirement.
Additional Information:
- Delivery Time: 1 TO 2 WEEKS
- Packaging Details: PLASTIC PACKING MATERIALS